Mechanical Properties of the Combined Single Lap-Shear Connections with Graphene Doped Epoxy Adhesives
Necati    ATABERK1*, Mürsel    EKREM2, Yasin    ÖZDEMİR3
1Necmettin Erbakan University  , Konya  , Turkey
2Necmettin Erbakan University  , Konya  , Turkey
3Necmettin Erbakan University  , Konya  , Turkey
* Corresponding author: nataberk@erbakan.edu.tr

Presented at the 3rd International Symposium on Innovative Approaches in Scientific Studies (Engineering and Natural Sciences) (ISAS2019-ENS), Ankara, Turkey, Apr 19, 2019

SETSCI Conference Proceedings, 2019, 4, Page (s): 640-643 , https://doi.org/

Published Date: 01 June 2019    | 376     8

Abstract

In this study, it is aimed to strengthen epoxy with graphene as an adhesive, because of recently the outstanding
properties of graphene. For this purpose, the effects of graphene usage on shear strength of modified epoxy-based adhesives
were examined. The shear strengths of the created bondings are investigated. For this goal, Al 2024-T3 sheet was used as a
bonding material. While determining the mechanical properties of graphene-doped epoxy based adhesives, the experiments
were carried out in accordance with ASTM D1002-10, single lap sheared connection. In order to carry out these processes,
surface treatment of aluminum plates, formation of adhesive materials, bonding process and drawing casting of lap-shear
samples to measure shear strength were applied respectively. Graphene were used in 0.25, 0.50, 0.75, 1% by weight. Five (5)
samples were produced from each sample for the reliability of the experiments. Morphological structure and diameters of the
formed samples were analyzed by scanning electron microscopy (SEM) images. The shear strength of the epoxy-based
adhesive by adding Graphene resulted in an increase when compared to neat epoxy. On the other hand, the ultimate shear
strain of the modified adhesives decreased by adding the nano particles into the epoxy resin.  

Keywords - Graphene, Epoxy, Shear Strenght, SEM, Lap-Shear

References

[1] Kozma, L. and I. Olefjord, Basic processes of surface preparation and bond formation of adhesively joined aluminium. Materials Science and Technology. 3(10): p. 860-874, 1987

[2] Lapique, F. and K. Redford, Curing effects on viscosity and mechanical properties of a commercial epoxy resin adhesive. International journal of adhesion and adhesives. 22(4): p. 337-346, 2002

[3] Da Silva, L.F., A. Öchsner, and R.D. Adams, Handbook of adhesion technology, ed. Series,2011. Springer Science & Business Media,

[4] Shao, H. and R.J. Stewart, Biomimetic underwater adhesives with environmentally triggered setting mechanisms. Advanced materials. 22(6): p. 729-733, 2010

[5] Coleman, J.N., et al., Improving the mechanical properties of singlewalled carbon nanotube sheets by intercalation of polymeric adhesives. Applied Physics Letters. 82(11): p. 1682-1684, 2003

[6] Banea, M. and L.F. da Silva, The effect of temperature on the mechanical properties of adhesives for the automotive industry. Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications. 224(2): p. 51-62, 2010

[7] Ban, G., et al., Effect of nano-Cu addition on microstructure evolution of Sn0. 7Ag0. 5Cu-BiNi/Cu solder joint. Soldering & Surface Mount Technology. 29(2): p. 92-98, 2017

[8] Ekrem, M., et al., Improving electrical and mechanical properties of a conductive nano adhesive. Journal of adhesion science and Technology. 31(7): p. 699-712, 2017

SETSCI 2024
info@set-science.com
Copyright © 2024 SETECH
Tokat Technology Development Zone Gaziosmanpaşa University Taşlıçiftlik Campus, 60240 TOKAT-TÜRKİYE