Stone Water Impregnation and Some Technological Properties in Various Impregnation / Diffusion Times of East Beech (Fagus Orientalis Link) Wood

Ulusoy

Hatice

Özderin

Sevgin

Nurgül

Muğla Sıtkı Koçman University Karadeniz Technical University

22 12 2019

9 529 531

2019

SET Technology

CC BY 4.0

In this study, some of the physıcal/mechanıcal properties of the wood were observed by impregnating the wood of East beech (Fagus orientalis Lipsky) with stone water named "Firetex" in accordance with ASTM 1413 76 standard. In this process, values of % retention, full dry / air mass specific gravity, bending resistance values are determined . According to the results of the experiment; highest retention at 45 min vacuum / 20 min diffusion (38.15 %), lowest 45 min vacuum at 30 min diffusion (29.73 %); the highest air dry weight was determined at 45 minutes vacuum at 20 minutes diffusion (0.75 g / cm3) and the highest full dry specific gravity at 45 minutes vacuum at 40 minutes diffusion (0.69 g / cm3); maximum bending resistance was determined at 45 minutes vacuum and 30 minutes diffusion (132.98 N / mm2).

Spruce Wood, Firetex (Stone Water), Impregnation, Retension, Furniture

Kartal, N., Engür, O., Köse, Ç., (2005) Emprenye Maddeleri ve Emprenye Edilmiş Ağaç Malzeme ile İlgili Çevre Problemleri, İstanbul Üniversitesi, Orman Fakültesi Dergisi, 17-23.

Tomak, E.D., ve Yıldız, Ü.C., (2012) Bitkisel Yağların Ahşap Koruyucu Bir Madde Olarak Kullanılabilirliği, Artvin Çoruh Üniversitesi, Orman Fakültesi Dergisi 13(1): 142-157.

Tomak, E.D., Cavdar, A.D., 2013. Limited oxygen index levels of impregnated Scots pine wood. Thermochimica acta, 573: 181-185.

Kesik, H.İ., Aydoğan, H., Çağatay, K., Özkan, O.E., Maraz, E., 2015. Fire Properties of Scots Pine Impregnated with Firetex. ICOEST International Conference on Environmental Science and Technology, Sarajevo, BH.

Özcan, C., Kurt, Ş., Esen, R., Korkmaz, M., 2016. The determinate combustion properties of fir wood impregnated with fire-retardants. The Online Journal of Science and Technology-July, 6(3).

TSE 2471 (1976) Odunda Fiziksel ve Mekaniksel Deneyler İçin Rutubet Tayini, TSE, Ankara.

TS 2472 (1976) Odunda, Fiziksel ve Mekaniksel Deneyler için Birim Hacim Ağırlık Tayini, TSE, Ankara

ASTM-D 1413-76 (1976). Standart test methods of testing wood preservatives by laboratory soilblock cultures, Annual Book of Astm Standarts. USA, 452-460.

TS 2474 (1976) Odunun Statik Eğilme Dayanımının Tayini.

Toker H., (2007) Borlu Bileşiklerin Ağaç Malzemenin Bazı Fiziksel Mekanik ve Biyolojik Özelliklerine Etkilerinin Belirlenmesi, Gazi Üniversitesi Fen Bilimleri Enstitüsü, Doktora Tezi, Eylül, Ankara

Atılgan, A ,Peker, H. (2012) Çeşitli Emprenye Maddelerinin Mobilya Ve Yapı Endüstrisinde Kullanılan Odun Türlerinin Bazi Fiziksel Özellikleri Üzerine Etkileri, Açü Faculty Of Forestry Journal,13(1):67-78.

Malkoçoğlu, A., (1994) Doğu Kayını (Fagus Orientalis Lipsky.) Odununun Teknolojik Özellikleri, KTÜ Fen Bilimleri Enstitüsü, Doktora Tezi, Trabzon.

Bozkurt, Y., Erdin, N., (1990) Ticarette Kullanılan Ağaçlarda Fiziksel ve Mekanik Özellikler, İ.Ü . Orman Fak. Dergisi, Seri B, 40, 1, 7-24, İstanbul.

Gür,İ., (2003) Emprenye İşleminin Sarıçam ve Kızılçamın Bazı Kekanik ve Fiziksel Özelliklerine Etkilerinin Belirlenmesi, Yüksek Lisans Tezi, Gazi Üniversitesi, Fen Bilimleri Enstitüsü, Ankara, 46-48.