Mechanical and Solubility Behavior of Chitosan Coated Hydroxyapatite Foams
Abstract
In this study highly porous hydroxyapatite foam fabricated by powder metallurgy method for various sintering temperatures and coated with chitosan after sintering. The solubility of the samples were in Lactated Ringer's solutions for various day. From the results compression strength developed from ⁓1.2 MPa to ⁓12 MPa. The pH of the solution was changed from ⁓7 to 7.45 and 7.28 for uncoated and chitosan coated samples. Finally, the sintered samples at 1150 oC for 2h showed the highest density and compressive strength.
Keywords
Cite this article
Dadaev, R. ., & Gürbüz, M. . (2019). Mechanical and Solubility Behavior of Chitosan Coated Hydroxyapatite Foams. In 3rd International Symposium on Innovative Approaches in Scientific Studies (Engineering and Natural Sciences) (pp. 632–633). SET Technology.